Synthesis, microstructure, anti-corrosion property and biological performances of Mn-incorporated Ca-P/TiO2composite coating fabricated via micro-arc oxidation

Loại tài liệu: Tài liệu số - Jounal article

Thông tin trách nhiệm: Xinxin Zhan

Nhà Xuất Bản:

Năm Xuất Bản: 2020

Chia sẻ

Tải ứng dụng tại các liên kết sau để xem đầy đủ tài liệu.

Tóm tắt

In this work, a Mn-incorporated Ca-P/TiO2composite coating was produced through the facile one-step micro-arc oxidation (MAO) method. It is revealed that only when the concentration of Na2Mn-EDTA reaches 0.02 mol/rnL, the Ca-P phase could form on Mn-incorporated TiO2coating, which is associated with the combined effect ofrnEDTA complex and Mn species. The Ca-P phase is amorphous, which may contain hydroxyapatite phasesrnwhereas the underlying Mn-incorporated TiO2coating contains two separate layers, including the Mn-rich outerrnlayer and Mn-depleted inner layer. The biological investigation of the Mn-incorporated Ca-P/TiO2compositerncoating suggests that it exhibits desirable osteogenesis with certain capability to inhibit the growth ofS. aureusrnbacteria. Hence, a promising composite coating with superior bone formability could be produced using the one-step micro-arc oxidation method in the electrolyte containing Na2Mn-EDTA.

Ngôn ngữ:en
Thông tin trách nhiệm:Xinxin Zhan
Thông tin nhan đề:Synthesis, microstructure, anti-corrosion property and biological performances of Mn-incorporated Ca-P/TiO2composite coating fabricated via micro-arc oxidation
Loại hình:Jounal article
Bản quyền:© 2020 Elsevier B.V. All rights reserved.
Mô tả vật lý:16p.
Năm Xuất Bản:2020

(Sử dụng ứng dụng VNU- LIC quét QRCode này để mượn tài liệu)

(Lưu ý: Sử dụng ứng dụng Bookworm để xem đầy đủ tài liệu. Bạn đọc có thể tải Bookworm từ App Store hoặc Google play với từ khóa "VNU LIC”)

  • Chủ đề
TÀI NGUYÊN KHÁC