Thông tin trách nhiệm: Hailin, Hea; Youping, Yi; Shiquan, Huang; Yuxun, Zhang
Nhà Xuất Bản: Elsevier
Năm Xuất Bản: 2019
Tải ứng dụng tại các liên kết sau để xem đầy đủ tài liệu.
The large 2219 Al alloy rings used to connect propellant tank components of a satellite launch vehicle to each other are conventionally manufactured by radial-axial ring rolling at 460◦C with 50% deformation, but often suffer from coarse elongated grain and low ductility. An improved process (hot ring rolling at 460◦ C with 30% deformation, then air cooling to 240◦ C, followed by ring rolling at 240◦C with 20% deformation) was tested for ring manufacturing. The corresponding microstructure evolution and mechanical properties of the produced rings were studied. The results show that the improved process can successfully be applied to manufacture the large 2219 Al alloy rings without formation of macroscopic defects, resulting in a product with fine and uniform grains after heat treatment. The fracture mechanism of both rings was mainly intergranular fracture. With the resulting grain size refinement due to the improved process, more homogeneous slip occured and the crack propagation path became more tortuous duringrnthe tensile testing process. Thus, the elongation in all three orthogonal directions was greatly improved, and the axial elongation increased from 3.5% to 10.0%.rn© 2018 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology
(Sử dụng ứng dụng VNU- LIC quét QRCode này để mượn tài liệu)
(Lưu ý: Sử dụng ứng dụng Bookworm để xem đầy đủ tài liệu. Bạn đọc có thể tải Bookworm từ App Store hoặc Google play với từ khóa "VNU LIC”)
Sport under Communism : behind the East German miracle
The political discourse of spatial disparities : geographical inequalities between science and propaganda
A practitioner's guide to state and local population projections
Thức tỉnh mục đích sống = A new earth - Awakening to your life's purpose : cuốn sách làm bừng tỉnh thế giới
Mornings in Florence
2-(Allyloxy) methylol-12-crown-4 ether functionalized polymer brushes from porous PolyHIPE using UV-initiated surface polymerization for recognition and recovery of lithium
Dependence of mechanical properties on the microstructure characteristics of a near titanium alloy Ti-7333
Heterogeneous form of poly (4-vinyl pyridine) beads based dendrimer stabilized Ag, Au and PdNPs catalyst for reduction of trypan blue
Nhảy moonwalk cùng Einstein: nghệ thuật và khoa học để nhớ được mọi thứ
Drugs During Pregnancy Methodological Aspects (1st ed. 2016)