Novel structural phase and superconductivity of W-Te compounds under high pressures

Loại tài liệu: Tài liệu số - Journal Article

Thông tin trách nhiệm: Chunying, Pu; Pei, Jiang; Rongmei, Yu; Ying, Xu; Changbo, Chen; Dawei, Zhou

Nhà Xuất Bản: Elsevier

Năm Xuất Bản: 2021

Chia sẻ
(Tải app tại đây để đọc sách)

Tóm tắt

Novel structural phase and superconductivity of W–Te compounds have been investigated using the developed particle swarm optimization algorithm in combination with ab initio calculations. Under ambient conditions, rnWTe2 with Td phase is the most stable. with the pressure increasing, the 2H phase becomes stable until 60 GPa, and then WTe2 decompose into Te and WTe with the Pm3m phase. More interesting, the layered Cmcm phase of WTe3 is obtained at about 6 GPa, which remains stable up to 100 GPa. Moreover, electron–phonon calculations have been performed, which suggest that the Cmcm phase of WTe3 is superconducting and the critical superconducting temperature can reach about 3 K at 10 GPa.

Ngôn ngữ:en
Thông tin trách nhiệm:Chunying, Pu; Pei, Jiang; Rongmei, Yu; Ying, Xu; Changbo, Chen; Dawei, Zhou
Thông tin nhan đề:Novel structural phase and superconductivity of W-Te compounds under high pressures
Nhà Xuất Bản:Elsevier
Loại hình:Journal Article
Bản quyền:www.elsevier.com/locate/commatsci
Mô tả vật lý:5 p.
Năm Xuất Bản:2021

(Sử dụng ứng dụng VNU- LIC quét QRCode này để mượn tài liệu)

(Lưu ý: Sử dụng ứng dụng Bookworm để xem đầy đủ tài liệu. Bạn đọc có thể tải Bookworm từ App Store hoặc Google play với từ khóa "VNU LIC”)

  • Chủ đề
TÀI NGUYÊN KHÁC