Chemically deposited PbS thin films by reaction media with glycine for use in photovoltaics

Loại tài liệu: Tài liệu số - Jounal article

Thông tin trách nhiệm: Yesica B. Castillo-S´ anchez, Luis A. Gonzalez

Nhà Xuất Bản:

Năm Xuất Bản: 2020

Chia sẻ

Tải ứng dụng tại các liên kết sau để xem đầy đủ tài liệu.

Tóm tắt

PbS thin films were chemically deposited on glass substrates using alkaline aqueous solutions containing glycinernPb complexes. Highly compact and adherent films, formed by pyramid-like particles, crystallized in the cubicrnstructure of galena-type PbS. The specular nature and compactness of the films was enhanced with the increase ofrnthe bath pH, as confirmed through the analysis of optical and electrical properties. The optical band gap energyrnand conductivity of the photosensitive PbS films were found in the range of 1.39–1.53 eV and 44.7 to 153.9 mS/rncm, respectively. The photovoltaic characteristics of CdS/PbS heterojunction devices were investigated. Thernphotovoltaic device with structure SnO2:F/CdS (~120 nm)/PbS(~180 nm)/C had an open circuit voltage of 120rnmV and a short circuit current density of 0.85 mA/cm2, under illumination intensity of 100 mW/cm2.

Ngôn ngữ:en
Thông tin trách nhiệm:Yesica B. Castillo-S´ anchez, Luis A. Gonzalez
Thông tin nhan đề:Chemically deposited PbS thin films by reaction media with glycine for use in photovoltaics
Loại hình:Jounal article
Bản quyền:© 2020 Elsevier Ltd. All rights reserved
Mô tả vật lý:8 p.
Năm Xuất Bản:2020

(Sử dụng ứng dụng VNU- LIC quét QRCode này để mượn tài liệu)

(Lưu ý: Sử dụng ứng dụng Bookworm để xem đầy đủ tài liệu. Bạn đọc có thể tải Bookworm từ App Store hoặc Google play với từ khóa "VNU LIC”)

  • Chủ đề
TÀI NGUYÊN KHÁC